70 Degree Lead Free Cable Wire PVC Compound
Posted on

Model NO.: 70degree 90 deegree
Trademark: longtai/jiangxi Anan
Specification: 70deg lead free PVC compound
Origin: China
HS Code: 39042200
Model NO.: 70degree 90 deegree
Trademark: longtai/jiangxi Anan
Specification: 70deg lead free PVC compound
Origin: China
HS Code: 39042200
1.Technical specifications of 70 ºC pvc compound
 
Tensile strength MPa 20.5
Fracture tensile strain % 320
Ageing temperature ºC 100
Ageing time h 168
Tensile strength after ageing MPa 22.5
Max change of tensile strength % +12
After ageing fracture tensile strain % 290
Max change of fracture tensile strain % -10
Thermal deformation % 28
Thermal ageing quality loss g/m2 19
200ºC thermal stability time min 90
20ºC volume resistivity  Ω.cm 2.0*1011
 
 
 
Technical specifications of  90 ºC pvc resin compound
 
Tensile strength MPa 20
Fracture tensile strain % 330
Ageing temperature ºC 100
Ageing time h 240
Tensile strength after ageing MPa 21.5
Max change of tensile strength % +8
After ageing fracture tensile strain % 310
Max change of fracture tensile strain % -6
Thermal deformation % 28
Thermal ageing quality loss g/m2 9
200ºC thermal stability time min 120
20ºC volume resistivity  Ω.cm 2.0*1010
 
2,Use and standard: wire and cable
 
3,Process: extrusion
 
4,Appearance: cylindrical particles,  plastication should be good, the color and luster is even, without obvious impurity.
 
5,color: Any colors, base on requirement.
 
6,Packing: 25kg net weight or 1000kgs per jumbo bag
70 Degree Lead Free Cable Wire PVC Compound

 
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
 
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting  compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.
70 Degree Lead Free Cable Wire PVC Compound
  1.Technical specifications of 70 ºC pvc compound
 
Tensile strength MPa 20.5
Fracture tensile strain % 320
Ageing temperature ºC 100
Ageing time h 168
Tensile strength after ageing MPa 22.5
Max change of tensile strength % +12
After ageing fracture tensile strain % 290
Max change of fracture tensile strain % -10
Thermal deformation % 28
Thermal ageing quality loss g/m2 19
200ºC thermal stability time min 90
20ºC volume resistivity  Ω.cm 2.0*1011
 
 
 
Technical specifications of  90 ºC pvc resin compound
 
Tensile strength MPa 20
Fracture tensile strain % 330
Ageing temperature ºC 100
Ageing time h 240
Tensile strength after ageing MPa 21.5
Max change of tensile strength % +8
After ageing fracture tensile strain % 310
Max change of fracture tensile strain % -6
Thermal deformation % 28
Thermal ageing quality loss g/m2 9
200ºC thermal stability time min 120
20ºC volume resistivity  Ω.cm 2.0*1010
 
2,Use and standard: wire and cable
 
3,Process: extrusion
 
4,Appearance: cylindrical particles,  plastication should be good, the color and luster is even, without obvious impurity.
 
5,color: Any colors, base on requirement.
 
6,Packing: 25kg net weight or 1000kgs per jumbo bag
70 Degree Lead Free Cable Wire PVC Compound

 
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
 
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting  compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.